s355jr-angle

S355JR, S355JR+AR Angle Bars, Equal Angle Bars, RSA-Rolled Steel Angle Bars

We are one of the major distributor of S355JR steel grade angle bar in the South East Asia Region as we understand your need and erectile dysfunction age want, our only objective is to Adenovirus infection Use Doxycycline let your projects achieve smooth completion with only 100% success allowed.

Beverly Steel specializes in wide range of BS EN10025-2 S355JR, S355JR+AR Equal Angle Bars from the origin of Thailand, Korea, Japan, China, Spain, Germany, UK, Brazil, USA, UAE and etc.. primarily to the structural construction, shipbuilding, bridge building, oil and gas, power plant, MRT - metro rail station, rail station, terminal, and other civil construction to general engineering.

Classifications

Mechanical Properties

BS EN 10025-2A : 2004 S355JR

Yield Point N/mm2 (min.)

Tensile Strength

Yield Ratio%

Elongation % (min.)

Impact

Thickness

N/mm2

(max.)

Thickness

Thickness ≥ 12mm.

t ≤ 16

16 < t ≤ 40

t ≤ 5

5 < t ≤ 16

t >16

Temp°C

Energy J (min.)

355

345

470-630

-

22

+20

27B



Classification

Chemical Compositions (ladle analysis), %

BS EN 10025-2A: 2004 S355JR

C

Si

Mn

P

S

CEC

SWD

Nb

V

N

Cu

Ni

Cr

Mo

Grain refining element

Micro-alloying element

max.

max.

max.

%max.

%max

max.

max.

max.

max.

max.

max.

max.

0.24

0.55

max.

1.60

max.

0.035

0.035

0.45EFG

-

-

-

0.012

0.55

-

-

-

-

-

A: Deliver condition type is +AR

B : Verified only when specified at the time of order

C : Carbon Equivalent :(JIS Version) CE = C+Mn/6+Si/24+Ni/40+Cr/5+Mo/4+V/14 (AS, ASTM, BS Standard)

CE=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15

D: Chemical composition on sensitivity of welding crank = C+Si/30+Mn/20+Cu/20+Ni/60+Cr/20+Mo/15+V/10+5B

E: The max. Carbon Equivalent for t > 30mm. is 0.47%

F: If Cu content is between 0.25 and 0.4%, the max. CE content shall be increased by 0.02%

G: If Si content < 0.030% the max. CE content shall be increase by 0.02% or if Si content < 0.25% the max. CE content shall be increased by 0.01%