S690QL High Strength Quenched and Tempered Structural Steel
S690QL High Strength Quenched and Tempered Structural Steel
S690QL Mechanical Properties
|
Plate Thickness |
Yield Strength |
Tensile Strength |
Elongation |
|
MM |
ReH(Mpa) |
Rm(Mpa) |
A5% Minimum |
|
3 to 50 |
690 |
770~940 |
14 |
|
> 50 to 100 |
650 |
760~930 |
14 |
|
> 100 to 150 |
630 |
710~900 |
14 |
S690QL V Notch Impact Test
|
Position of Samples |
0 degree C |
- 20 degree C |
-40 degree C |
|
Longitudinal |
50 Joules |
40 Joules |
30 Joules |
|
Transverse |
35Joules |
30 Joules |
27 Joules |
Processing of S690QL High Strength Steel Plate
S690QL Cold Forming
S690QL steel plate is real life health suitable for cold-forming adhering to a bending or folding radius > 4 times steel plate thickness longitudinal and go right here > 3 times transverse to rolling direction. A subsequent stress relief annealing is possible up to a temperature of 580 ºC (degree C).
|
Minimum recommended inside bending radius |
|
|
Axis of real health prostate formula review bend in transverse direction 3.0t |
Axis of bend in longitudinal direction 4.0t |
S690QL Hot-Forming
Hot-forming above 580°C is possible. A subsequent quenching and tempering has to be carried out according to the conditions of delivery.
S690QL Milling
Drilling with cobalt-alloyed high-speed steels HSSCO. Cutting speed should be approximately 17 - 19 m/min. If HSS drills are used, cutting speed should be approximately 3 – 5 m/min.